Worldwide, the most widely used system for prototype part and limited series manufacture
| TEST TYPE ISO | 8891 | 6095 | 8045 | 8045-1 | 8045-2 | 8045-3 | 8060-1 | 8060-2 | 8060-3 | SG-95 / SG-95 LP | 8051 | 8263 UL94 5VA | 9012 FDA wet & dry |
||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Description | – | Flexible rubber | Pe | PP | PP / PE | PP / PE | PE | PP / PE | PP / PE | PP / PE | ABS | ABS | ABS | ABS | |
| Properties | Soft | • | |||||||||||||
| Semi rigid | • | • | • | • | |||||||||||
| Rigid | • | • | • | • | • | • | • | • | |||||||
| High temp. | • | • | • | • | |||||||||||
| UV stable | • | ||||||||||||||
| FDA | • | ||||||||||||||
| Others | • | • | |||||||||||||
| Product colour at 25°C | – | White / translucent | Colourless / transparent | White / transparent | White / translucent | Slightly yellow / translucent | Colourless / transparent | White / opaque | White translucent | ||||||
| Hardness (Shore A/D) | 868 | 82 D | 74 D | 70 D | 61 D | 48 D | 80 D | 80 D | 80 D | 83 D | 77 D | ||||
| Flexural strength (MPa) | 178 | – | 80 | – | – | – | – | 60 | 48 | 64 | 99 | 95 | 93 | 51 | |
| Flexural modulus (MPa) | 178 | – | 2000 | – | – | – | – | 1310 | 1010 | 1320 | 2400 | 2200 | 2200 | 1310 | |
| Tensile modulus (MPa) | R 527 | – | – | 970 | 700 | 400 | 150 | 1225 | – | – | 2521 | 2150 | – | – | |
| Tensile strength (MPa) | R 527 | 2 – 17 | 60 | 32 | 24 | 12 | 10 | 47 | – | – | 58 | 63 | 68 | 40 | |
| Heat deflection temp °C (HDT) | – | – | 80 | 79 | 53 | 42 | 35 | 105 – 175 | 90 – 110 | 115 – 180 | 72 | 92 | 80 | 90 | |
| Glass transition temp °C (Tg) | – | – | 110 | – | – | – | – | 127 – 195 | 105 – 132 | 125 – 195 | 68 | 90 | – | 108 | |
| Elongation yield (%) | – | – | – | – | – | – | – | – | – | – | 6 | 5 | – | – | |
| Elongatoin at break (%) | R 527 | 270 – 330 | 30 | 55 | 60 | 65 | 75 | 43 | – | – | 25 | 18 | 15 | 25 | |
| Tear strength (MPa) | 34 | 7 – 34 | – | – | – | – | – | – | – | – | – | – | – | – | |
| Yield strength (MPa) | R 527 | – | – | – | – | – | – | – | – | – | 64.2 | 62 | – | – | |
| Izod impact (kJ/m2) | 180 | – | 10 | – | – | – | – | 14 | 15 | 13 | 12 | 16 | 10 | – | |
| Thermal conductivity (W/mK) | – | – | – | – | – | – | – | – | – | 0.208 | 0.225 | 7 | – | ||
| Specific gravity (kg/dm3 at 25 °C) | – | 1.0 | 1.05 | 1.07 | 1.07 | 1.07 | 1.07 | 1.03 | 1.03 | 1.03 | 1.07 | 1.12 | 1.3 | 1.10 | |
| – | 1.16 | 1.09 | 1.16 | 1.16 | 1.16 | 1.16 | 1.21 | 1.21 | 1.21 | 1.19 | 1.19 | 1.19 | 1.12 | ||
| – | 0.99 | – | – | 0.99 | 0.99 | 0.99 | – | – | – | – | – | – | – | ||
| Viscosity (cPs at 25°C) | Part A | – | 470 | 1200 | 1000 | 1000 | 1000 | 1000 | 220 | 220 | 220 | 1300 | 7550 | 1000 | 1500 |
| Part B | – | 170 | 140 | 220 | 220 | 220 | 220 | 50 | 50 | 50 | 130 | 180 | 160 | 150 | |
| Part C | – | 90 | – | – | 90 | 90 | 90 | – | – | – | – | – | – | – | |
| Mixing ratio by weight (A:B:C) | – | 100:100:0 – 300 | 100:150 | 100:140 | 100:140:25 | 100:140:50 | 100:140:75 | 100:400 | 100:250 | 100:500 | 100:150 | 100:200 | 100:150 | 29:100 | |
| Pot life sec. (100g at 25°C) | – | 200 – 360 | 480 | 345 | 320 | 300 | 270 | 285 | 270 | 330 | 300 | 300 | 360 | 720 | |
| Demoulding time (at 70°C) (hrs) | – | 1.0 | 1.0 | 1.0 | 1.0 | 1.0 | 1.0 | 1.0 | 1.0 | 0.5 | 0.75 | 0.75 | 1.0 | 2.0 | |
| Shrinkage (%) according to wall thickness | – | 1.0 | 0.3 | 0.4 | 0.4 | 0.4 | 0.4 | 0.5 | 0.5 | 0.5 | 0.2 | 0.2 – 0.3 | 0.3 | 0.5 – 1.0 | |
| Product | Cured Colour | Shore Hardness (A/D) @23°C | De-mould Time (mins) @70°C | Heat Deflection (°C) | Glass Transition (°C) | Flexural Modulus (N/mm2) | Properties (see individual data sheets for full technical specifications) |
|---|---|---|---|---|---|---|---|
| 8891 | White / Translucent | 20 A – 90 A | 60 | – | – | – | Low viscosity flexible rubber: completely ajustable hardness. Shoe soles, Gaskets, Hoses. |
| 6095 | Colourless / Translucent | 82 D | 60 | 80 | 110 | 2000 | Suitably strong for snap fits. Perfectly Clear, UV-stabilised for colour matching. |
| 8045 | White / Transparent | 74 D | 60 | 79 | – | – | PP/PE Type. High impac. Snap fits. Pigmentable. |
| 8045-1 | Clear / Transparent | 70 D | 60 | 53 | – | – | PP/PE type. Variable hardness properties. Pigmentable. Suitable for high impact snap fit applications. |
| 8045-2 | Clear / Transparent | 61 D | 60 | 42 | – | – | PP/PE type. Variable hardness properties. Pigmentable. Suitable for high impact snap fit applications. |
| 8045-3 | Clear / Transparent | 48 D | 60 | 35 | – | – | PP/PE type. Variable hardness properties. Pigmentable. Suitable for high impact snap fit applications. |
| 8060-1 | Transparent / Yelowish | 80 D | 60 | 105 – 175* | 127 – 195 | 1310 | Similar to PP/PE. High heat resistance . Very high impact stength. |
| 8060-2 | Transparent / Yelowish | 80 D | 60 | 90 – 110 | 105 – 132 | 1010 | Similar to PP/PE. High heat resistance . Very high impact stength. |
| 8060-3 | Transparent / Yelowish | 80 D | 30 | 115 – 180 | 125 – 195 | 1320 | Similar to PP/PE. High heat resistance . Very high impact stength. |
| SG95 | Colourless / Transparent | 74 D – 82 D | 45 | 72 | 68 | 2400 | Excellent all round ABS type properties. Suitably strong for snap fits. Perfectly Clear for colour matching. |
| SG95 LP | Colourless / Transparent | 74 D – 82 D | 45 | 72 | 68 | 2400 | Excellent all round ABS properties. Suitably strong for snap fits. 100 % perfect for colour matching. Long pot life for producing very large thin walled components up to 10 Kg. |
| 8051 | White / Translucent | 77 D – 84 D | 45 | 92 | 90 | 2200 | ABS Type: High heat stability. Strong flexing properties. |
| 8263 | White / Translucent | 83 D | 60 | 80 | – | 2200 | Flame retardent, good impact strength. Certified fire retardent UL94 – VO. Suitable for electrical enclosures. |
| 9012 | White opaque | 77 D | 120 | 90 | 108 | 1310 | Simulates ABS. Compliant to both dry and wet food FDA requirements. |
Download Safety Data Sheets
All information is based on results gained from experience and tests and is believed to be accurate but is given without acceptance of liability for loss or damage attributable to reliance thereon. Users should always carry out sufficient tests to establish the suitability of any products for their intended applications.
* After post curing schedule (see individual datasheets).